The photo-oxidation of 3,4-dihydroxy-cinnamic acid (DHCA) is investigated on TiO2 films prepared from commercial Degussa P-25 (FP25 films) and from colloidal TiO2 prepared by the sol-gel method (FSG films). Photo-oxidation rates have been found to be inversely correlated to the amount of adsorbed species. The extent of adsorption increases as the solution pH increases from 1 to 4 and is more pronounced in the case of FP25 samples for which the amount of adsorbed species is 2.7 × 10-10 mol cm-2, i.e. about threefold higher than for the FSG case. Analysis of DHCA adsorption on TiO2 suspensions provided information complementary to that collected on films. Diffuse reflectance UV-visible and FTIR spectra of adsorbed DHCA are conspicuously different for the two types of films. © 2009 Elsevier B.V. All rights reserved.
Adsorption and photo-oxidation of 3,4-dihydroxy-cinnamic acid on TiO2 films
AMADELLI, Rossano;MALDOTTI, Andrea;
2009
Abstract
The photo-oxidation of 3,4-dihydroxy-cinnamic acid (DHCA) is investigated on TiO2 films prepared from commercial Degussa P-25 (FP25 films) and from colloidal TiO2 prepared by the sol-gel method (FSG films). Photo-oxidation rates have been found to be inversely correlated to the amount of adsorbed species. The extent of adsorption increases as the solution pH increases from 1 to 4 and is more pronounced in the case of FP25 samples for which the amount of adsorbed species is 2.7 × 10-10 mol cm-2, i.e. about threefold higher than for the FSG case. Analysis of DHCA adsorption on TiO2 suspensions provided information complementary to that collected on films. Diffuse reflectance UV-visible and FTIR spectra of adsorbed DHCA are conspicuously different for the two types of films. © 2009 Elsevier B.V. All rights reserved.I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.