The thermal evolution process of RuO2–SnO2/Ti mixed oxide thin films of varying noble metal content has been investigated by thermogravimetry–mass spectrometry and Fourier transform infrared emission spectroscopy. The gel-like films prepared from aqueous solutions of the precursor salts Sn(OH)2(CH3COO)2−xClx and Ru(OH)Cl3 on titanium metal support were heated in an atmosphere containing 20% O2 and 80% Ar up to 873 K. Chlorine evolution takes place in a single stage process between 573 and 773 K, while the decomposition of organic species like various types of carbonyls, carbonates and carboxylates occurs in two main stages between 423 and 773 K. The combustion temperature of the organic species formed decreases with the increase of the ruthenium content, indicating the catalytic effect of the noble metal. The secondary processes can significantly influence the morphology and electrochemical properties of the films when used as anodes in electrochemical processes.
Investigation of RuO2-SnO2 thin film formation by thermogravimetry-mass spectrometry and infrared emission spectroscopy
VAZQUEZ GOMEZ, Lourdes;DE BATTISTI, Achille
2006
Abstract
The thermal evolution process of RuO2–SnO2/Ti mixed oxide thin films of varying noble metal content has been investigated by thermogravimetry–mass spectrometry and Fourier transform infrared emission spectroscopy. The gel-like films prepared from aqueous solutions of the precursor salts Sn(OH)2(CH3COO)2−xClx and Ru(OH)Cl3 on titanium metal support were heated in an atmosphere containing 20% O2 and 80% Ar up to 873 K. Chlorine evolution takes place in a single stage process between 573 and 773 K, while the decomposition of organic species like various types of carbonyls, carbonates and carboxylates occurs in two main stages between 423 and 773 K. The combustion temperature of the organic species formed decreases with the increase of the ruthenium content, indicating the catalytic effect of the noble metal. The secondary processes can significantly influence the morphology and electrochemical properties of the films when used as anodes in electrochemical processes.I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.