The effect of copper (Cu) addition up to 3.2 wt% on crack initiation and propagation in an Al–Si–Mg cast alloy was investigated using in-situ cyclic testing in the as-cast condition. A combination of digital image correlation, electron backscatter diffraction, and scanning electron microscopy was used to investigate crack initiation and propagation behaviour during in-situ cyclic testing. The results showed that Cu-rich intermetallic compounds with the addition of Cu up to 1.5 wt% do not affect the fatigue behaviour of these alloys, and that crack propagation in these cases is trans-granular and trans-dendritic. However, increasing the concentration of the Cu retained in the primary α-Al matrix in solid solution and Cu-containing precipitates delayed crack propagation during cyclic testing. The results showed that strain accumulation was highest at the grain boundaries; however, the crack preferred to propagate along or across primary α-Al dendrites due to the relatively lower mechanical strength of the matrix compared to the eutectic and intermetallic phases. Moreover, the addition of Cu of more than 3.0 wt% to Al-Si-Mg alloys changes the fatigue behaviour that a rapid failure occurs.

The influence of copper addition on crack initiation and propagation in an Al–Si–Mg alloy during cyclic testing

Lattanzi L.
Secondo
;
Merlin M.;
2020

Abstract

The effect of copper (Cu) addition up to 3.2 wt% on crack initiation and propagation in an Al–Si–Mg cast alloy was investigated using in-situ cyclic testing in the as-cast condition. A combination of digital image correlation, electron backscatter diffraction, and scanning electron microscopy was used to investigate crack initiation and propagation behaviour during in-situ cyclic testing. The results showed that Cu-rich intermetallic compounds with the addition of Cu up to 1.5 wt% do not affect the fatigue behaviour of these alloys, and that crack propagation in these cases is trans-granular and trans-dendritic. However, increasing the concentration of the Cu retained in the primary α-Al matrix in solid solution and Cu-containing precipitates delayed crack propagation during cyclic testing. The results showed that strain accumulation was highest at the grain boundaries; however, the crack preferred to propagate along or across primary α-Al dendrites due to the relatively lower mechanical strength of the matrix compared to the eutectic and intermetallic phases. Moreover, the addition of Cu of more than 3.0 wt% to Al-Si-Mg alloys changes the fatigue behaviour that a rapid failure occurs.
2020
Bogdanoff, T.; Lattanzi, L.; Merlin, M.; Ghassemali, E.; Seifeddine, S.
File in questo prodotto:
File Dimensione Formato  
1-s2.0-S2589152920302039-main.pdf

solo gestori archivio

Descrizione: post print
Tipologia: Post-print
Licenza: NON PUBBLICO - Accesso privato/ristretto
Dimensione 3.57 MB
Formato Adobe PDF
3.57 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
1-s2.0-S2589152920302039-main_EDITORIALE.pdf

accesso aperto

Descrizione: versione editoriale
Tipologia: Full text (versione editoriale)
Licenza: Creative commons
Dimensione 7.44 MB
Formato Adobe PDF
7.44 MB Adobe PDF Visualizza/Apri

I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11392/2432855
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 10
  • ???jsp.display-item.citation.isi??? 9
social impact