Lithium-sulfur (Li-S) batteries are promising candidates for next generation electrical energy storage devices due to their high specific energy. Despite intense research, there are still a number of technical challenges in developing a high performance Li-S battery. To elucidate the issues, an all solid-state Li-S battery was fabricated using Li3PS4 solid electrolyte. Most of the theoretical capacity of sulfur, 1600 mAhg−1 was attained in the initial discharge-charge cycles with a high coulombic efficiency approaching 99%. To verify the benefit of the solid state electrolyte, galvanostatic stripping-deposition tests were also carried out on a symmetrical Li/Li cell and compared with those of a liquid electrolyte (1M- lithium bis(trifluoromethane sulfonyl) imide (LiTFSI) in a mixture of 1,3-dioxolane (DOL)-diethoxyethane (DEE)). The kinetics and thermodynamics of the solid-state cell are discussed from the viewpoint of the charge transfer processes. This study demonstrates both the merits and drawbacks of using the solid sulfide electrolyte in a Li-S battery and facilitates the further improvement of this important high energy storage device.
All solid-state lithium-sulfur battery using a glass-type P2S5-Li2S electrolyte: Benefits on anode kinetics
HASSOUN, Jusef;
2015
Abstract
Lithium-sulfur (Li-S) batteries are promising candidates for next generation electrical energy storage devices due to their high specific energy. Despite intense research, there are still a number of technical challenges in developing a high performance Li-S battery. To elucidate the issues, an all solid-state Li-S battery was fabricated using Li3PS4 solid electrolyte. Most of the theoretical capacity of sulfur, 1600 mAhg−1 was attained in the initial discharge-charge cycles with a high coulombic efficiency approaching 99%. To verify the benefit of the solid state electrolyte, galvanostatic stripping-deposition tests were also carried out on a symmetrical Li/Li cell and compared with those of a liquid electrolyte (1M- lithium bis(trifluoromethane sulfonyl) imide (LiTFSI) in a mixture of 1,3-dioxolane (DOL)-diethoxyethane (DEE)). The kinetics and thermodynamics of the solid-state cell are discussed from the viewpoint of the charge transfer processes. This study demonstrates both the merits and drawbacks of using the solid sulfide electrolyte in a Li-S battery and facilitates the further improvement of this important high energy storage device.File | Dimensione | Formato | |
---|---|---|---|
Yamada_2015_J._Electrochem._Soc._162_A646.pdf
accesso aperto
Descrizione: versione editoriale
Tipologia:
Full text (versione editoriale)
Licenza:
Creative commons
Dimensione
773.5 kB
Formato
Adobe PDF
|
773.5 kB | Adobe PDF | Visualizza/Apri |
I documenti in SFERA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.